Formation of optical planar waveguides on fused quartz by MeV ion implantation

 

Resumen. The optical losses and the refractive index change of optical planar waveguides formed by MeV ion implantation were correlated with the experimental ion implantation parameters. Direct ion implantation was performed by means of carbon, silicon and copper ion beams impinging on the substrate surface at normal incidence. The ions were accelerated at energies ranging from 3 to 12 MeV with fluences varying from 1 × 1012 to 2 × 1016 ion/cm2, according to the type of implanted ion. The modification of the substrate refractive index due to the ion irradiation-induced damage was evaluated using the prism coupler method, and the refractive index profiles were determined by means of a reconstruction method using a multilayer structure approximation. The guiding properties of the waveguides were analysed using the fibre-coupling technique to determine both the optical transmission and transversal modes at 635 nm. The main practical relevance of our research is the obtention of high-quality waveguides at low current density MeV ion implantation (≤80 nA/cm2) without post-implantation annealing.

Autores. Yuriy Kudriavtsev
Revista. IET Optoelectronics
https://doi.org/10.1049/ote2.12114

Print
CONTÁCTENOS

Logo Cinvestav

Av. Instituto Politécnico Nacional 2508
Col. San Pedro Zacatenco, Alcaldía Gustavo A. Madero
Ciudad de México, C.P. 07360
Apartado Postal: 14-740, 07000 Ciudad de México

Tel. +52 (55) 5747 3800

Cinvestav © 2024
23/09/2024 02:20:25 p. m.